High-temperatureFluid Loss Control Agent

1 sku

High-temperatureFluid Loss Control Agent

Technical parameters

1. Appearance; Light brown liquid;
2. Density; 1.08;
3. Solubility; Water soluble;
4. PH; 6.5-7.5.

Executive standard

Q/HYZOK 0004-2015

Supply capability

Brand : HYZOK

Guarantee period : 6 Months from receiving qualified goods.

Enquiry Now
High-temperatureRetarder(CM026)

1 sku

High-temperatureRetarder(CM026)

Technical parameters

1. Appearance; Colorless liquid;
2. Density; 1.08;
3. Solubility; Water soluble;
4. Melting point/flashpoint>100℃.

Executive standard

Q/HYZOK 0007-2015

Supply capability

Brand : HYZOK

Guarantee period : 6 Months from receiving qualified goods.

Enquiry Now
Viscous Spacer

1 sku

Viscous Spacer

Technical parameters

1. Appearance; Gray powder;
2. Density; 1.78;
3. Solubility; Water soluble;
4. Melting point/flashpoint>93℃.

Executive standard

Q/HYZOK 0005-2015

Supply capability

Brand : HYZOK

Guarantee period : 6 Months from receiving qualified goods.

Enquiry Now
Anionic Polyacrylamide

2 sku

Anionic Polyacrylamide

Technical parameters

1. White crystal;
2. Content; ≥90%;
3. Moisture; ≤10%;
4. Hydrolysis Degree; 20%-30%;
5. Molecular Weight; 18x106-25x106;
6. Apparent Viscosity; According to the customer's requirement;
7. Undissolved Substance; ≤0.2%;
8. Dissolving Time; ≤2h;
9. Flocculation Time; ≤0.1h;
10. Granularity; Less than 0.15mm ≤5%, more than 1.5mm ≤2%.

Executive standard

Q/0500JSH010-2013

Supply capability

Brand : SHUIHENG

Guarantee period : 24 Months

Enquiry Now
XP-1 Defoamer for Oil Well Cement

1 sku

XP-1 Defoamer for Oil Well Cement

Technical parameters

1、Appearance: colorless or yellowish viscous liquid;
2、Recovery rate of cement slurry density ≥90%

Executive standard

Q/CPOCL 0406-2016

Supply capability

Brand : OCL

Guarantee period : Kept away from fire, damage and leakage in store and transportation. Storage life time is one years.

Enquiry Now
GH-Ⅰ Middle Temperature Retarder for Oil Well Cement

1 sku

GH-Ⅰ Middle Temperature Retarder for Oil Well Cement

Technical parameters

1、Appearance: Pale yellow powder;
2、Water content,% ≤10.0;
3、Fineness (0.315mm sieve),% ≤10.0;
4、Initial consistrency , Bc ≤30;
5、Mutation value of thickening curve,Bc ≤10;
6、Thickening time/120℃.73.9Mpa.61min ,Adjustable;
7、Free liquid,% ≤1.4;
8、Compression strength, Mpa/144℃,21Mpa,48h ≥14; The ingredient of the cement slurry in the table is: G class: cement ,W/C 0.44,
Dosage of GH-I: 0.1%~1.0% ,Water quality: distilled water

Executive standard

Q/CPOCL 0219-2017

Supply capability

Brand : OCL

Guarantee period : Be kept away from moisture and possible damage of the packages in transportation, be stored in cool and dry situation. Storage life time is two years.

Enquiry Now
Low Chromium Ferrochrome Lignosulfonate

1 sku

Low Chromium Ferrochrome Lignosulfonate

Technical parameters

1. Appearance: dark brown powder;
2. Moisture: 8.5% or less;
3.pH value (1% water solution): 3.0-4.5;
4. Iron content: 2.8%-3.2%.
5. Chrome content: 2.1%-2.5%;

Executive standard

Q/MHLHG15-2013

Supply capability

Brand : JINFENG

Guarantee period : 12 months from the date of delivery

Enquiry Now
G310 Fluid Loss Control Additives for Oil Cement

1 sku

G310 Fluid Loss Control Additives for Oil Cement

Technical parameters

1. Appearance: viscous liquid;
2. Initial consistency (80 ℃ .46.5Mpa.45min) ≤30Bc;
3. Thickening linear: normal;
4.40Bc ~ 100Bc time ≤ 40min;
5. Water loss (80 ℃ .6.9MPa.30min) ≤ 150ml;
6. Compressive strength (102 ℃ .21 MPa.24h) ≥ 14MPa.
The above cement slurry formula: G grade cement, specific gravity of 1.90g / cm3, water: distilled water, 5.0% G310.

Executive standard

Q/CPOCL 0217-2017

Supply capability

Brand : OCL

Guarantee period : 12 months from thedelivery date of the product

Enquiry Now
G204 Early Strength Additive for Oil Well Cement

1 sku

G204 Early Strength Additive for Oil Well Cement

Technical parameters

1. Appearance: white or light yellow powder;
2. Water content ≤ 8.0%;
3. Fineness (0.315mm after screening) ≤ 15.0%;
4. Initial consistency ≤ 30Bc;
5. Thickening time ≤ blank slurry thickening time under the same conditions;
6. Compressive strength (50 ℃, 24h) ≥ 6 Mpa,;
7. Compressive strength (50 ℃, 48h) ≥ 8Mpa; cement slurry formula: grade G cement: microsphere = 100: 10: 5, W/ C (water cement ratio): 0.70, 2.0% G204 (BWOS), water quality: distilled water.

Executive standard

Q/CPOCL 0206-2017

Supply capability

Brand : OCL

Guarantee period : Within 24 months after production

Enquiry Now
G209-L Early Strength Additive for Oil Well Cement

1 sku

G209-L Early Strength Additive for Oil Well Cement

Technical parameters

1. Appearance: soil yellow liquid;
2. Initial consistency < 30Bc;
3, Thickening time, min / 30 ℃ and atmospheric pressure. 15 min < protoplasmic;
4. 8 h (30 ℃) compressive strength≥4MPa;
5. 24 h (30 ℃)compressive strength≥12MPa;
Water mud formula: grade G cement, W/C:0.44, G209-L: 2.5%(BWOC), water quality: 4% salt water.

Executive standard

Q/CPOCL 0209-2017

Supply capability

Brand : OCL

Guarantee period : Within 24 months after production

Enquiry Now